Jagannath, Gangareddy and Eraiah, Bheemaiah and Gaddam, Anuraag and Fernandes, Hugo and Brazete, Daniela and Jayanthi, K and Krishnakanth, Katturi Naga and Rao, Soma Venugopal and Ferreira, Jose M F and Annapurna, K and Allu, Amarnath R (2019) Structural and Femtosecond Third-Order Nonlinear Optical Properties of Sodium Borate Oxide Glasses: Effect of Antimony. Journal of Physical Chemistry C, 123 (9). pp. 5591-5602. ISSN 1932-7447

PDF - Published Version Restricted to Registered users only Download (1635Kb) | Request a copy

Abstract

Structural and optical properties of antimony-containing sodium borate glasses were studied and their ultrafast third-order nonlinear optical (NLO) properties have been evaluated using Z-scan measurements with femtosecond (fs) pulses (similar to 150 fs, 80 MHz) at 750, 800, and 880 nm wavelengths. Glasses in the (mol %) 20Na(2)O (80 - x)B2O3 - xSb(2)O(3) (where x = 0, 10, 20, and 30) system have been fabricated via melt quench technique. The structural modifications were analyzed using the Raman and magic angle spinning (MAS)-nuclear magnetic resonance (NMR) (B-11 MAS-NMR and Na-23 MAS-NMR) techniques. The optical absorption spectra revealed that the absorption edge was red-shifted, suggesting the decrease in band gap energy with increase of antimony content in the glasses. Raman scattering results revealed that the boroxol rings are depressed with the incorporation of Sb2O3 for replacing B2O3. B-11 MAS-NMR results showed a progressive increase of B-4 units at the expense of B-3 units. The Raman and B-11 MAS-NMR results support the formation of Sb5+ ions due to oxidation of Sb3+ that played the role of charge compensation. Na-23 MAS-NMR spectra revealed a decreasing trend in the average of bond lengths of Na-O with increasing Sb2O3 contents. This suggested that sodium changed its role from charge compensator to modifier cation. The antimony-containing glasses demonstrated a reverse saturable absorption in open-aperture Z-scan mode due to two-photon absorption, while closed-aperture Z-scan signatures depicted positive nonlinear refraction due to self-focusing effect. The NLO coefficients were found to increase with Sb2O3 due to the increased nonbridging oxygens and also due to the hyperpolarizability of Sb3+ and Sb5+ ions. The observed NLO data clearly suggest that the investigated glasses are beneficial for optical limiting applications.

Item Type:	Article
Subjects:	Glass
Divisions:	Glass
Depositing User:	Bidhan Chaudhuri
Date Deposited:	14 Nov 2019 09:36
Last Modified:	14 Nov 2019 09:36
URI:	http://cgcri.csircentral.net/id/eprint/4604

Actions (login required)

View Item