Nath, Mithun and Ghosh, A and Tripathi, Himansu Sekhar (2016) Hot corrosion behavior of Al2O3-Cr2O3 refractory by molten glass at 1200 degrees C under static condition. Corrosion Science, 102. pp. 153-160. ISSN 0010-938X

[img] PDF - Accepted Version
Restricted to Registered users only

Download (3544Kb) | Request a copy

Abstract

Hot corrosion behavior of Al2O3-Cr2O3 refractory by molten glass at 1200 degrees C under static condition was monitored. Glass-refractory interface was investigated by XRD, SEM and EDX analysis. After 36h of testing, no visible change was observed, but SEM analysis revealed a corroded region of 315 mu m. Corrosion occurs via dissolution of Al2O3 followed by mass exchange and formation of Fe2O3-Cr2O3 solid solution, which acts as a barrier to the molten glass. However, the Cr2O3 fractions of the refractory remained uncorroded. (C) 2015 Elsevier Ltd. All rights reserved.

Item Type: Article
Subjects: Refractories
Divisions: Refractory
Depositing User: Bidhan Chaudhuri
Date Deposited: 27 Oct 2016 07:19
Last Modified: 27 Oct 2016 07:19
URI: http://cgcri.csircentral.net/id/eprint/3611

Actions (login required)

View Item View Item