Das, Mitun and Bhattacharya, Kaushik and Dittrick, Stanley A. and Mandal, Chitra and Balla, Vamsi Krishna and Kumar, T S Sampath and Bandyopadhyay, Amit and Manna, Indranil (2014) In situ synthesized TiB-TiN reinforced Ti6Al4V alloy composite coatings: Microstructure, tribological and in-vitro biocompatibility. Journal of the Mechanical Behavior of Biomedical Materials, 29 (SI). pp. 259-271. ISSN 1751-6161

[img] PDF - Published Version
Restricted to Registered users only

Download (1386Kb) | Request a copy

Abstract

Wear resistant TiB-TiN reinforced Ti6Al4V alloy composite coatings were deposited on Ti substrate using laser based additive manufacturing technology. Ti6Al4V alloy powder premixed with 5 wt% and 15 wt% of boron nitride (BN) powder was used to synthesize Til3-TiN reinforcements in situ during laser deposition. Influences of laser power, scanning speed and concentration of BN on the microstructure, mechanical, in vitro tribological and biological properties of the coatings were investigated. Microstructural analysis of the composite coatings showed that the high temperature generated due to laser interaction with Ti6Al4V alloy and BN results in situ formation of Till and TiN phases. With increasing EN concentration, from 5 wt% to 15 wt%, the Young's modulus of the composite coatings, measured by nanoindentation, increased from 170 +/- 5 GPa to 204 +/- 14 GPa. In vitro tribological tests showed significant increase in the wear resistance with increasing BN concentration. Under identical test conditions TiB-TiN composite coatings with 15 wt% BN exhibited an order of magnitude less wear rate than CoCrMo alloy a common material for articulating surfaces of orthopedic implants. Average top surface hardness of the composite coatings increased from 543 +/- 21 HV to 877 +/- 75 HV with increase in the BN concentration. In vitro biocompatibility and flow cytometry study showed that these composite coatings were non-toxic, exhibit similar cell-materials interactions and biocompatibility as that of commercially pure titanium (CP-Ti) samples. In summary, excellent in vitro wear resistance, high stiffness and suitable biocompatibility make these composite coatings as a potential material for load-bearing articulating surfaces towards orthopaedic implants. (C) 2013 Elsevier Ltd. All rights reserved.

Item Type: Article
Subjects: Engineering Materials
Divisions: Bioceramics & Coating
Depositing User: Bidhan Chaudhuri
Date Deposited: 18 Dec 2014 09:46
Last Modified: 18 Dec 2014 09:46
URI: http://cgcri.csircentral.net/id/eprint/2660

Actions (login required)

View Item View Item