Mukhopadhyay, Anoop Kumar and Chakraborty, D (1988) Influence on some factors on strength and fracture toughness of reaction bonded silicon nitride. Transactions of the Indian Ceramic Society, 47 (2). pp. 36-42. ISSN 0371-750X

[img] PDF - Published Version
Restricted to Registered users only

Download (594Kb) | Request a copy

Abstract

Influence of density, Young's modulus, temperature and other experimental variables on strength and fracture toughness of reaction bonded silicon nitride (RBSN) was studied. Fractographic study was made to identify the nature of flaws. The density dependence of strength could be expressed through proposed empirical equations. Strength of RBSN was proportional to Young's modulus. In the range RT-1400°C some RBSN had constant strength, while others had a peak in strength at 1200°C followed by degradation at 1400°C. The density dependence of fracture toughness could be expressed through some equations. Fracture toughness of RBSN had direct dependence on strength and Young's modulus. High temperature fracture toughness and strength were directly dependent on each other. Fracture toughness of RBSN at RT increased as notch tip radius was increased in the range 79–225 μm, but it did not show any systematic variation as the normalized notch length was varied.

Item Type: Article
Subjects: Engineering Materials
Divisions: UNSPECIFIED
Depositing User: Bidhan Chaudhuri
Date Deposited: 25 Nov 2013 13:31
Last Modified: 05 Mar 2016 13:18
URI: http://cgcri.csircentral.net/id/eprint/2302

Actions (login required)

View Item View Item