Sarkar, Soumya and Das, Probal Kumar (2012) Statistical analysis of mechanical properties of pressureless sintered multiwalled carbon nanotube/alumina nanocomposites. Materials Chemistry and Physics, 137 (2). pp. 511-518. ISSN 0254-0584

PDF - Published Version Restricted to Registered users only Download (2218Kb) | Request a copy

Abstract

Mechanical properties of pressureless sintered 0.15-1.2 vol. multiwalled carbon nanotube reinforced alumina matrix nanocomposites have been analyzed using the 2-parameter Weibull statistics. Electron microscopy and phase analysis of nanocomposites sintered at 1700°C for 2 h in Argon revealed existence of interpenetrating network of nanotubes in alumina, formation of thin interface resembling stoichiometric aluminum monoxycarbide and matrix grain refinement by nanotubes. Statistical analyses indicated that with increasing Vickers hardness testing load (4.9-19.6 N) and flexural strength measurement temperature (room temperature to 1100°C), Weibull modulus of nanocomposites increased significantly suggesting improved consistency at higher load and temperature. The highest Weibull moduli were obtained for nanocomposites containing either 0.15 or 0.3 vol. nanotube which were �40 and �15 higher than single phase alumina for hardness and strength, respectively, supporting the specimen size effect on reliability of present brittle ceramic matrix nanocomposites. Superior mechanical reliability of nanocomposites over pure alumina was primarily attributed to the presence of structurally intact nanotubes forming effective interface region to ensure proper load sharing, matrix grain refinement, and especially, at higher testing load and temperature, overall averaging effect of flaws to yield higher Weibull moduli. © 2012 Elsevier B.V. All rights reserved.

Item Type:	Article
Uncontrolled Keywords:	Alumina matrix; Averaging effect; Brittle ceramics; Higher loads; Interface regions; Load sharing; Matrix grains; Mechanical reliability; Phase analysis; Pressureless-sintered; Room temperature; Single phase; Size effects; Weibull modulus; Weibull statistics, Aluminum; Composite materials; Electron microscopes; Electron microscopy; Grain refinement; Grain size and shape; Load testing; Mechanical properties; Multiwalled carbon nanotubes (MWCN); Nanocomposites; Nanotubes; Sintering; Statistical methods; Vickers hardness testing; Weibull distribution, Sintered alumina
Subjects:	Engineering Materials
Divisions:	Non-Oxide Ceramics & Composites
Depositing User:	Bidhan Chaudhuri
Date Deposited:	07 Feb 2013 13:19
Last Modified:	07 Feb 2013 13:19
URI:	http://cgcri.csircentral.net/id/eprint/1882

Actions (login required)

View Item