Seal, A and Mazumder, R and Sen, Amarnath and Maiti, Himadri Sekhar
(2006)
Fast firing of lead zirconate titanate ceramics at low temperature.
Materials Chemistry and Physics, 97 (1 ).
14-18 .
ISSN 0254-0584
Abstract
A fast firing technique for densification of PZT (up to 97% of theoretical density) at a low temperature (950 degrees C) has been found out. A small amount of excess PbO (3-5 wt.%) and a fast firing schedule are required to achieve the desired sintering. The final composition of the sintered ceramics can be kept close to the morphorropic phase boundary by modifying the firing time and post-sintering annealing treatment at 800 degrees C. The g(33) values of fast fired samples are comparable to those of conventionally sintered samples, though the d(33) values are somewhat lower than those reported for conventionally sintered (at 1250'C or above) samples
| Item Type: |
Article
|
| Uncontrolled Keywords: |
dielectric properties; piezoelectricity; electronic materials; fast-firing |
| Subjects: |
UNSPECIFIED |
| Divisions: |
UNSPECIFIED |
| Depositing User: |
Mrs Chandana Patra
|
| Date Deposited: |
05 Jan 2012 05:43 |
| Last Modified: |
15 May 2016 13:18 |
| URI: |
http://cgcri.csircentral.net/id/eprint/190 |
Actions (login required)
 |
View Item |
![[img]](http://cgcri.csircentral.net/style/images/fileicons/application_pdf.png)