Rajan, S Thanka and Das, Mitun and Arockiarajan, A (2023) In vitro assessment of corrosion resistance and biocompatibility of tantalum-niobium oxide surface-functionalized Mg alloy. Materials Chemistry and Physics, 301. Art No-127560. ISSN 0254-0584

[img] PDF - Published Version
Restricted to Registered users only

Download (12Mb) | Request a copy


Magnesium alloys have been considered as temporary biomaterials for orthopedic applications. Despite having great mechanical (bone-like) characteristics and osseointegration, magnesium alloys deteriorate quickly in physiological conditions. Modifying the Mg alloy surface with tantalum-based thin films is an effective process to reduce the rate of corrosion and improve biocompatibility. In the present work, tantalum-niobium oxide nanocomposite thin films were successively deposited on Mg-Al6-Zn1.5-Cu2-Ge0.5 Mg alloys via reactive magnetron sputtering to improve anticorrosion and biocompatibility. Crystallographic structure, surface morphology and chemical compositions were characterized using XRD, TEM, FE-SEM, EDS and XPS. Electrochemical and hydrogen evolution experiments were used to evaluate the resistance to corrosion of the samples. The biocompatibility of the samples was evaluated by cell viability using the osteoblast cell line (MC3T3-E1). Results revealed the existence of the composite thin-film in the crystalline form and the cauliflower-like clustered morphology. Enhancement in the corrosion resistance of nanocomposite coatings was confirmed by a decrease in current density (Icorr) during the polarization studies. The wettability studies revealed the hydrophilic character of the coatings and they are bioactive in simulated body fluid (SBF) after 5 days by the mineralization of calcium phosphate. The hemocompatibility assessment proved that the coatings were blood compatible in nature. MTT (3-(4, 5-dimethylthiazolyl-2)-2, 5-diphenyltetrazolium bromide) assay on MC3T3-E1 cells showed that tantalumniobium oxide thin films are biocompatible and can stimulate cellular proliferation and differentiation. Overall,

Item Type: Article
Subjects: Engineering Materials
Divisions: Bioceramics & Coating
Depositing User: Bidhan Chaudhuri
Date Deposited: 06 Oct 2023 12:20
Last Modified: 06 Oct 2023 12:20
URI: http://cgcri.csircentral.net/id/eprint/5571

Actions (login required)

View Item View Item